ZEONET® PB
什么是ZEONET®PB
ZEONET®PB是FKM(氟橡胶)和NBR(丁腈橡胶)的硫化型粘合剂。
- 工业上常见需要FKM和NBR粘合的场面。NBR加ZEONET®PB可以大幅提高 FKM和NBR的粘结强度。
- ZEONET®PB适用于FKM的多元醇/胺/一氧化铅硫化等体系，提高硫化 粘结力。
- ZEONET®PB适用NBR的硫磺/过氧化物硫化体系。
- ZEONET®PB适用FKM和ECO的硫化粘合。
Adhesion test of FKM and PVC modified NBR
Tested rubber
FKM: Viton® VTR9160PVC modified NBR: Nipol® DN508
Applied curing recipe
| FKM | |
|---|---|
| Viton® VTR9160 | 100 |
| Bisphenol F | Originally contained in Viton® VTR9160 |
| MgO | 6 |
| Ca(OH)2 | 6 |
| Carbon black: N762 | 15 |
| PVC modified NBR | ||
|---|---|---|
| Sulfur cure | Peroxide cure | |
| Nipol® DN508 | 100 | 100 |
| ZnO#1 | 5 | 5 |
| Stearic acid | 1 | 1 |
| Carbon black: N990 | 30 | 30 |
| Nipsil VN3 | 15 | 15 |
| Thiokol TP95 | 15 | 15 |
| A.O.224 | 2 | 2 |
| Wax | 2 | 2 |
| Sulfur | 1.5 | - |
| TMTD |
0.5 | - |
| MBTS | 1.5 | - |
| Percumil D-40 | - | 2 |
Adhesion test result
| NBR cure system | Sulfur | Peroxide | ||
|---|---|---|---|---|
| ZEONET® PB for NBR cure | 0 | 3PHR | 0 | 3PHR |
| Failure mode at peeling test | A.F. | M.B. | A.F. | M.B. |
M.B.: Material Break
Effect of ZEONET® PB on mechanical properties of cured NBR
| NBR cure system | Sulfur | Peroxide | |||
|---|---|---|---|---|---|
| ZEONET® PB for NBR cure | 0 | 3PHR | 0 | 3PHR | |
| Mooney Scorch @125 degrees C t5 (min.) |
16.2 | 4.8 | 11.4 | 9.7 | |
| Tensile properties |
Tensile Strength (MPa) | 15.6 | 17.2 | 16.4 | 17.3 |
| Elongation (%) | 420 | 190 | 280 | 470 | |
| 100% Modulus (MPa) | 3.3 | 8.2 | 4.2 | 3.5 | |
| Hardness (Shore A) | 71 | 77 | 37 | 44 | |
| Compression Set (%) 70hr.s at 100 degrees C |
47 | 67 | 37 | 44 | |
- 本产品是一般工业产品，在用于食用，医疗等特殊用途时，务必请事先确认，在安全的基础上，进行使用。
- 产品使用者请遵守MSDS上的操作处置规范和现行的相关法律与法规。
- 本资料中的数据只供参考，不能用作最终使用数据。